Ключевые слова: HTS, GdBCO, EuBCO, bulk, joints, fabrication, melting, trapped field, microstructure, susceptibility, critical caracteristics, Jc/B curves, experimental results
Ключевые слова: HTS, GdBCO, bulk, ErBCO, joints, pulsed magnetization, critical caracteristics, Jc/B curves, trapped field distribution, experimental results
Sakai N., Yokoyama K., Oka T., TAKEMURA K., Dorget R., Sudo K., Dadiel J.L., Sakafuji M., *1Murakami M.
Ключевые слова: HTS, GdBCO, bulk, joints superconducting , fabrication, melting, sintering, ErBCO, pulsed magnetization, trapped field distribution, Jc/B curves
Ключевые слова: HTS, GdBCO, bulk, joints superconducting , EuBCO, trapped field distribution, Jc/B curves, pulsed magnetization
Ключевые слова: MgB2, bulk, perforated sample structure, magnets, pulsed magnetization, flux jumps, degradation studies, trapped field, experimental results
Ключевые слова: NMR magnet, relaxation, gradient, HTS, REBCO, bulk, magnets, pulsed magnetization, activation energies, experimental results
Sakai N., Oka T., Ishida S., Ogino H., Eisaki H., Naik S.P., Nishio T., Peczkowski P., Ishibashi S., Hagiwara R.
Ключевые слова: HTS, YBCO, bulk, single grain, fabrication, seeding technique, irradiation effects, ultrasonic methods, susceptibility, critical caracteristics, Jc/B curves
Ключевые слова: MgB2, bulk, powder processing, acoustic emission, pinning, fabrication, critical caracteristics, critical current density, microstructure
Sakai N., Leveque J., Koblischka M.R., Berger K., Ayat S., Colle A., Nouailhetas Q., Dorget R., Sudo K., Douine T.O.
Ключевые слова: Maglev system, fabrication, magnetization, levitation performance, HTS, SmBCO, bulk, flux density, distribution, stiffness, damping, experimental results
Ключевые слова: HTS, GdDyBCO, infiltration process, fabrication, seeding technique, single grain, bulk, nanodoping, nanoparticles, nanoscaled effects, trapped field, pinning, microstructure, X-ray diffraction, lattice parameter, susceptibility, resistive transition, critical temperature, resistivity, temperature dependence, critical current density, experimental results
Murakami M., Sakai N., Jirsa M., Noudem J., Murakami A., Naito T., Miryala M., Mochizuki H., Arvapalli S.S., Fujshiro H.
Ключевые слова: MgB2, bulk, fabrication, sintering, pulsed magnetization, mechanical properties, X-ray diffraction, susceptibility, critical caracteristics, critical current density, temperature dependence, Jc/B curves, pinning force, stress effects, strain effects, trapped field, bending process, trapped field distribution
Ogawa J., Sakai N., Yokoyama K., Oka T., Noudem J., Hassler W., Berger K., Miryala M., Yamanaka K., Dadiel L., Sudo K., Murakami M
Ключевые слова: MgB2, bulk, fabrication, hot pressing, doping, magnets, pulsed magnetization, trapped field, shielding effects, penetration depth, thickness dependence, experimental results
Murakami M., Sakai N., Yokoyama K., Oka T., Nakano T., Miryala M., Ooizumi M., Seki H., Tsujimura M., Dadiel L., Sudo K., Furusawa M.
Ключевые слова: magnetic separation, HTS, GdBCO, bulk, magnets, measurement setup, pulsed magnetization, experimental results
Sakai N., Oka T., Ogino H., Naik S.P., Peczkowski P., Dadiel J.L., Sugiyama J., Kazuya Y., Warski T., Wojcik A., Murakami T.O.
Ключевые слова: bearing magnetic, new, HTS, GdBCO, bulk, YBCO, coated conductors, coils, permanent magnets, pulsed operation, damping, measurement setup, displacements, stiffness, experimental results
Ogawa J., Nakamura T., Murakami M., Fukui S., Sakai N., Yokoyama K., Oka T., Takahashi M., Inoue N., Miryala M., Tsunoda S.
Ключевые слова: NMR magnet, HTS, SmBCO, bulk, pulsed magnetization, magnetic flux distribution, uniformity, trapped field distribution, experimental results
Murakami M., Sakai N., Oka T., Jirsa M., Muralidhar M., Rao M.S., TAKEMURA K., Sunsanee P., Srikanth A.S.
© Copyright 2006-2012. Использование материалов сайта возможно только с обязательной ссылкой на сайт.
Свои замечания и пожелания вы можете направлять по адресу perst@isssph.kiae.ru
Техническая поддержка Alexey, дизайн Teodor.